Biprint®: Biplex® corrugated sheet for the printing industry

Biprint® is the ideal printing medium. It’s double-sided corona treatment allows easy printing, even for digital printing. Biprint® is resistant to moisture, is strong and light-weight. This makes Biprint® the perfect substrate for outside and inside applications. The corona treatment also provides a better adhesion when gluing the sheets to other materials, or when using adhesives. Biprint® can easily be cut or die-cut and can be converted into virtually any shape.

Biprint® is extruded from polypropylene copolymer, it is much more durable than cardboard and is completely recyclable.
  • easily printable
  • water and moisture resistant
  • strong and durable
  • light-weight

Applications

  • Real estate signs

  • Real estate signs

  • Publicity panels

  • Publicity panels

  • Promotional items

  • Construction site-boards

Other applications:

Temporary signs, displays, POS displays, promotional & merchandising items, …

Characteristics

  • economic Economic
  • reusable Reusable
  • strong & durable Strong & durable
  • good rupture & tear resistance Good rupture & tear resistance
  • washable Washable
  • Online bedrukken van uw logo / tekst Easily printable
  • ecological Ecological
  • water & moisture resistant Water & moisture resistant
  • good chemical resistance Good chemical resistance
  • light-weight Light-weight
  • food approved Food approved
  • corona treatment Corona treatment

Treatments

  • flame retardant Flame retardant
  • UV stabilizer UV stabilizer
  • antistatic Antistatic

Processing

  • cutting (guillotine, manual, plotter) Cutting (guillotine, manual, plotter)
  • die cutting Die cutting
  • welding (thermal, ultrasonically, hot air) Welding (thermal, ultrasonically, hot air)
  • bonding Bonding
  • sterilising Sterilising
  • recycling Recycling
  • cleaning Cleaning
  • stapling Stapling
  • printing Printing

Specifications

PHYSICAL PROPERTIES

Specific gravity PP ISO 1183 g/cm3 0,907
Water absorption ISO 62 % 0,02

MECHANICAL PROPERTIES

Tensile strength (50 mm/min) ISO 527 MPa 38
Elongation at break (50 mm/min) ISO 527 % 800
Flexural modulus ISO 178 MPa 1250
Impact strength Izod (23°C) ISO 180 kJ/m² 80
Shore D hardness ISO 868 - 66
Compression strength at maximum 2,1mm/350g Internal IPB N/cm² min. 37
Compression strength at maximum 2,0mm/400g Internal IPB N/cm² min. 41
Compression strength at maximum 3,0mm/600g Internal IPB N/cm² min. 70
Compression strength at maximum 3,0mm/650g Internal IPB N/cm² min. 55
Compression strength at maximum 3,0mm/400g Internal IPB N/cm² min. 30
Compression strength at maximum 3,5mm/650g Internal IPB N/cm² min. 80
Compression strength at maximum 3,5mm/700g Internal IPB N/cm² min. 78
Compression strength at maximum 3,5mm/800g Internal IPB N/cm² min. 140
Compression strength at maximum 4,5mm/1000g Internal IPB N/cm² min. 144

THERMAL PROPERTIES

Coefficient of linear expansion ASTMD696 mm/m°C 0,18
Specific Heat DSC J/g°C 1,68
Heat deflection temp.(0,46 MPa) ISO 75 °C 78
Heat deflection temp.(1,82 MPa) ISO 75 °C 52
Vicat softening point (1 kg) (10N) ISO 306 °C 148
Vicat softening point (5 kg) (50N) ISO 306 °C 78

OPTICAL PROPERTIES

Light transmission (clear sheet) 2,0mm/400g Internal IPB % 58
Light transmission (clear sheet) 2,5mm/450g Internal IPB % 53
Light transmission (clear sheet) 3,0mm/500g Internal IPB % 51
Light transmission (clear sheet) 4,0mm/1000g Internal IPB % 37

ELECTRICAL PROPERTIES

Surface resistivity ASTMD257 Ω ca. 1013
Dielectric constant (at 1 MHz) ASTMD150 - 2,25
Dissipation factor (tgδ at 1MHz) ASTMD150 - < 5 x 10-4
Dielectric strength (500V/sec) ASTMD149 kV/mm 70